White High-Temperature Fiberglass Cloth High Silica Fiberglass Fabric For Industry
1. Description:
High-silicon fiberglass cloth is a good fireproof material, which can be widely used in industry, and its high-temperature resistance can reach 1000℃. The silica content is above 96%. The weave style is satin. Smooth and soft. We can cut it easily. All fiberglass fabrics are woven for fiber orientation, and each has its own unique weight, strength, and fabric characteristics that should be considered before starting any project.
2. Technique Data Sheets for High Silica Cloth
| 1 | WEAVE | SATIN 8HS | Testing Method |
| 2 | Width | 92cm | 36.2inch | DIN EN 1773 |
| 100cm | 39.4inch |
| 86cm | 33.1inch |
| 3 | SiO2 Content | ≥96% | - |
| 4 | Linear shrinkage ( 1000C 30min) | <7.10% | - |
| 5 | Area Shrinkage( 1000C 30min) | <13.0% | - |
| 6 | Color | White / Golden | - |
| 7 | Thickness | 1.3±0.1mm | 0.051inch | DIN EN ISO 5084 |
| 8 | Treatment | Hydrochloric acid treatment | - |
| 9 | Weight | 1100g/m2 | 32.4OZ/YD2 | DIN EN 12127 |
| 10 | Thread count | WARP | 20 per cm | 51 per inch | DIN EN 1049-2 |
| WEFT | 15 per cm | 38 per inch | DIN EN1049-2 |
| 11 | Tensile strength | WARP | ≥1100 | EN ISO 13934-1 |
| N/Inch | WEFT | ≥900 | EN ISO 13934-1 |
| 12 | Service temperature | Up to 1100ºC | - |
3. Features:
1. SiO2 Content ≥ 96%
2. Excellent Heat Resistance, 1000oC
3. Low Thermal Conductivity
4. No Asbestos, Harmless to Human Body
5. Good Electrical Insulation
6. Low Thermal Shrinkage
4. Application:
Welding blanket and fire curtains
High-temperature resistance, thermal protection, and fire protection
Protective shields during welding works
5. Product Detail Images
6. More Silica Cloth Specification
| Product Name | Model | Width mm | Working Temperature℃ | Weight g/㎡ | SiO2 Content |
| High Silica | JNHS-300-92 | 92 | 1000 | 300 | ＞96% |
| High Silica | JNHS-450-92 | 92 | 1000 | 450 | ＞96% |
| High Silica | JNHS-600-92 | 92 | 1000 | 612 | ＞96% |
| High Silica | JNHS-600-100 | 100 | 1000 | 612 | ＞96% |
| High Silica | JNHS-600-130 | 130 | 1000 | 612 | ＞96% |
| High Silica | JNHS-880-92 | 92 | 1000 | 880 | ＞96% |
| High Silica | JNHS-880-100 | 100 | 1000 | 880 | ＞96% |
| High Silica | JNHS-1100-92 | 92 | 1000 | 1100 | ＞96% |
| High Silica | JNHS-1100-100 | 100 | 1000 | 1100 | ＞96% |
| Silica Cloth | JNSC-450-100 | 100 | 800 | 600 | 70%±5% |
| Silica Cloth | JNSC-600-92 | 92 | 800 | 600 | 70%±5% |
| Silica Cloth | JNSC-600-100 | 100 | 800 | 700 | 70%±5% |
| Silica Cloth | JNSC-600-152 | 152 | 800 | 700 | 70%±5% |
| Silica Cloth | JNSC-1100-92 | 92 | 800 | 1100 | 70%±5% |
| Silica Cloth | JNSC-1200-100 | 100 | 800 | 1200 | 70%±5% |
| Silica Cloth | JNSC-1200-152 | 152 | 800 | 1200 | 70%±5% |
| High Silica Texturized Cloth | JNSCT-42-92 | 92 | 1000 | 1450 | ＞96% |
| High Silica Texturized Cloth | JNSCT-42-100 | 100 | 1000 | 1450 | ＞96% |